Alumina Ceramic Filler High Alumina Inert Ball/99% alumina ceramic polo
Tulaga Fa'aletino ma Vailaau Fa'asao ole Polo Ceramic Inert
| O mea fa'aletino ma kemikolo o polo sima leisa | |||||||
| Elemene | Al2O3％ | 60 | 70 | 80 | 90 | 95 | 99 |
| Fe2O3％ | ≤0.9 | ≤0.8 | ≤0.6 | ≤0.4 | ≤0.3 | ≤0.1 | |
| O vaega o totoe e mafai ona fuafuaina e ala i feutagaiga i le va o le faʻatau ma le faʻatau pe a manaʻomia. | |||||||
| mitiia vai,％ | 3± 1, E mafai foi ona fuafuaina e ala i feutagaiga i le va o le faʻatau ma le faʻatau | ||||||
| fua, kg/m³ | 2.5-3.0 | 2.7-3.2 | 2.9-3.2 | ≥3.1 | ≥3.2 | ≥3.4 | |
| Tulaga tele, kg/m³ | 1400-1550 | 1400-1650 | 1500-1800 | 1700-1950 | 1800-1950 | ≥1900 | |
| Pefu, ta'e pe malepe | O se ato e tasi e itiiti ifo i le 5% | ||||||
| Fua'iga ese'ese | Polofesa tutusa, o le fua faatatau o le tele i le laʻititi laʻititi o le sima sima e le sili atu i le 1.2 | ||||||
| Fa'apalepale vaega | ≤10mm | ±1.0 | |||||
| 11—25mm | ±1.5 | ||||||
| 26—50mm | ±2.0 | ||||||
| ≥50mm | ±3.0 | ||||||
| Malosi pa'u sa'oloto | fua faatatau leai se gau ≥99％ | ||||||
| Malosi fa'amalosi | φ3 | ≥250 | ≥300 | ≥350 | ≥400 | ≥500 | ≥500 |
| φ6 | ≥800 | ≥1000 | ≥1000 | ≥1200 | ≥1500 | ≥1500 | |
| φ8 | ≥1500 | ≥1600 | ≥1800 | ≥2000 | ≥2500 | ≥2500 | |
| φ10 | ≥2000 | ≥2500 | ≥2800 | ≥3000 | ≥3500 | ≥3500 | |
| φ13 | ≥3000 | ≥3000 | ≥3500 | ≥4000 | ≥5000 | ≥5000 | |
| φ16 | ≥3500 | ≥4000 | ≥4500 | ≥5000 | ≥6000 | ≥7000 | |
| φ20 | ≥6000 | ≥6000 | ≥7000 | ≥8000 | ≥10000 | ≥12000 | |
| φ25 | ≥7000 | ≥7000 | ≥8000 | ≥10000 | ≥15000 | ≥17000 | |
| φ30 | ≥8000 | ≥9000 | ≥10000 | ≥12000 | ≥17000 | ≥19000 | |
| φ38 | ≥10000 | ≥12000 | ≥13000 | ≥15000 | ≥20000 | ≥22000 | |
| φ50 | ≥12000 | ≥14000 | ≥16000 | ≥18000 | ≥22000 | ≥26000 | |
| φ75 | ≥16000 | ≥18000 | ≥20000 | ≥22000 | ≥25000 | ≥30000 | |
| 50-75 | 55-75 | 60-80 | ≥80 | ≥82 | ≥85 | ||
| La'ei % | ≤2 | ≤1 | |||||
| soluble acid,％ | ≤6 | ||||||
| Alkali,％ | ≥77 | ≥85 | ≥90 | ≥92 | ≥95 | ≥97 | |
| Refractoriness，℃ | ≥400 | ≥500 | ≥700 | ≥1000 | ≥1000 | ≥1000 | |
| E tetee i le eseesega o le mamafa faʻafuaseʻi | Le faʻaleagaina fua ≥ 99%, leai se suiga i le malosi faʻamalosi ma le mamafa pe a maeʻa suiga faʻafuaseʻi e itiiti ifo i le 25% | ||||||
| Tete'e i suiga fa'afuase'i o le vevela | Fua'iga leai se gau≥99% | ||||||
| afifi | afifiina pusa u'amea | Faʻapipiʻi i pusa uʻamea, faʻamaufaʻailogaina i pusa palasitika PP poʻo PE mafiafia | |||||
| afifiina ato lalaga | E maua i taga lalaga malosi ma fa'asa'o i le UV | ||||||
| Fa'aaliga: O fa'amaumauga fa'atele e mo na'o fa'amatalaga, ae le o se fa'avae mo le taliaina. | |||||||
O le isi Fa'amatalaga: Va'ai le Laulau 5 Mo le Suavai o le 99 Fa'atumu Polo
| 99 Faatumuina o Polo Suavai | ||
| 99 fa'atumu | lautele | lautele |
| lola faia | φ＜25mm | ＜5％ |
| Fausia masini lolomi | φ＞25mm | <10% |
99.5% Fa'ailoga Fa'apitoa
| Al2O3 | ≥99% |
| SiO2 | ≤0.14% |
| Fe2O3 | ≤0.04% |
| CaO +MgO | ≤0.03% |
| TiO2 | ≤0.06% |
| Na2O | ≤0.1% |
| K2O | ≤0.1% |
Fa'asinomaga Fa'aletino ole Polo Fa'atumu Vailaau
| TULAGA | FA'asinomaga |
| fa'amaluluina o uta (yb/t370-1995) | Deformation i lalo ole 0.2mpa mamafa e itiiti ifo i le 0.6% |
| Tete'e te'i vevela (yb/t376.2-1995) | 1200°C i lalo i le 600°C. 10 taimi e aunoa ma ni ta'ei luga |
| Toe susunu laina suiga (gb/t3997.1-1998) | 1400 ℃ mo le 12 itula, o le tau maualuga o le 0.25%, o le averesi tau e itiiti ifo i le 0.20% |
| Tele tele (gb/t2997-2000) | 3.2-3.50 g/cm3 |
| malosi nutimomoia | Feiloai e sili atu i le 230 kg/cm2 |
| E aliali mai le porosity | 12-18% |
| Fa'atosina tele | 2.1-2.3g/cm3 |
Fa'apipi'i Polo Fa'ameamea
1) Fa'apipi'i masani: ato lalaga polyethylene ma le mamafa o le 25kg, fa'atasi ai ma fata.
2) Faʻapipiʻi paʻu uamea: 100L pusa uʻamea uʻamea, e mafai ona faʻaopoopo pallets